Bio-based content of biomass and petroleum products measured by accelerated mass spectrometry based on ASTM D6866
2007
Kunioka, Masao
The biobassed contents of raw materials such as starches, sugar, chitin, or wood powders for biomass plastics were measured using Accelerated Mass spectrometry (AMS) based on ASTM D6866. AMS measures the isotope carbon ratio of 14C to 12C and 13C in graphite derived front sample powders. The biobased contents of starches, sugar or chitin were almost 100 %, which means that they are fully biobased. The biobased contents of the wood powders were over 140 % due to the effect of the post 1950's 14 C injection due to nuclear testing. Poly(Ɛ-caprolactone) (PCL) composite samples were prepared using the polymerizalion and direct molding method. The starting compound was the Ɛ-caprolactone monomer liquid combined with cellulose and inorganic fillers using aluminium triflate as a catalyst at 80 °C for 6 or 24 hours. PCL cylinder-shapedcomposite samples with a homogeneously dispersed cellulose filler were prepared with Mn - 4600 (Mw/Mn = 2.9). The biobased content of the PCL composite with 50 wt% cellulose filler (51.67 %) measured using time was ,slightly higher than the carbon ratio of cellulose in the starting powder samples (41.3 mol%) This is is due to the higher biobased content (112.70%) of the cellulose filler used in this study. The biobased content of the polymer composite powders by AMS was found to be effected by the presence of inorganic fillers, such as talc.
اظهر المزيد [+] اقل [-]الكلمات المفتاحية الخاصة بالمكنز الزراعي (أجروفوك)
المعلومات البيبليوغرافية
تم تزويد هذا السجل من قبل Universiti Putra Malaysia