Using biodegradable pins, sternal cartilage autografts were fixed into osteochondral defects of the distal radial carpal bone in ten 2 to 3-year-old horses. The defects measured 1 cm2 at the surface and were 4 mm deep. Control osteochondral defects of contralateral carpi were not grafted. After confinement for 7 weeks, horses were walked 1 hour daily on a walker for an additional 9 weeks. Horses were euthanatized at 16 weeks. Half of the repair tissue was processed for histologic and histochemical (H&E and safranin-O fast green) examinations. The other half was used for the following biochemical analyses: type-I and type-II collagen contents, total glycosaminoglycan content, and galactosamine-to-glucosamine ratio. On histologic examination, the repair tissue in the grafted defects consisted of hyaline-like cartilage. Repair tissue in the nongrafted defects consisted of fibrocartilaginous tissue, with fibrous tissue in surface layers. On biochemical analysis, repair tissue of grafted defects was composed predominantly of type-II collagen; repair tissue of nongrafted defects was composed of type-I collagen. Total glycosaminoglycan content of repair tissue of grafted defects was similar to that of normal articular cartilage. Total glycosaminoglycan content of nongrafted defects was 62% of that of normal articular cartilage (P < 0.05). Repair tissue of all defects was characterized by galactosamine-to-glucosamine ratio significantly (P < 0.05) higher than that of normal articular cartilage. These results at 16 weeks after grafting indicate that sternal cartilage may potentially constitute a suitable substitute for articular cartilage in large osteochondral defects of horses.

Periosteal autograft were used for repair of large osteochondral defects in 10 horses aged 2 to 3 years old. In each horse, osteochondral defects measuring 1.0 X 1.0 cm2 were induced bilaterally on the distal articular surface of each radial carpal bone. Control and experimental defects were drilled. Periosteum was harvested from the proximal portion of the tibia and was glued into the principal defects, using a fibrin adhesive. Control defects were glued, but were not grafted. Sixteen weeks after the grafting procedure, the quality of the repair tissue of control and grafted defects was assessed biochemically. Total collagen content and the proportion of type-II collagen were determined. Galactosamine and glucosamine contents also were determined. From these measurements, contents of chondroitin and keratan sulfate and total glycosaminoglycan, and galactosamine-to-glucosamine ratio were calculated. All biochemical variables were compared with those of normal equine articular cartilage taken from the same site in another group of clinically normal horses. Total collagen content was determined on the basis of 4-hydroxyproline content, using a colorimetric method. The proportions of collagen types I and II in the repair tissue were assessed by electrophoresis of their cyanogen bromide-cleaved peptides on sodium dodecyl sulfate slab gels. Peptide ratios were computed and compared with those of standard mixtures of type-I and type-II collagens. Galactosamine and glucosamine contents were determined by use of ion chromatography. In general, the biochemical composition of repair tissue of grafted and nongrafted defects was similar, but clearly differed from that of normal articular cartilage. Total glycosaminoglycan content, galactosamine and glucosamine contents, and galactosamine-to-glucosamine ratio of grafted and nongrafted defects were all significantly (P < 0.05) less than corresponding values in normal equine articular cartilage. By contrast, total collagen content of neocartilaginous tissues of grafted and nongrafted defects was greater than that of normal articular cartilage, although the difference was not significant. The proportion of type-I and type-II collagens in repair tissue in grafted and nongrafted defects was 70 and 30%, respectively. The fibrous nature of the repair tissue reported in a companion morphologic and histochemical study was substantiated by the biochemical results. We concluded that use of periosteal autograft did not improve the healing of osteochondral defects.

Edible bird's nest (EBN)is made from the saliva of swiftlet from the Aerodramus species. It is one of the most widely consumed traditional health food by the Chinese community due to its claimed medicinal value. EBN contains glycoproteins with abundance of sialic acid (SA). EBN with higher SA content has a potential to command for higher price. The objective of this study was to determine and compare free SA content of EBN collected from Johor and Kelantan. A total of 23 and 30 of raw and unprocessed EBN samples were obtained from Kelantan and Johor, respectively. SA from EBN samples were analysed using LC-MS/MS. Johor showed higher content of free SA with the value of 135.04 ± 29.60 mg/kg compared to Kelantan which has a value of 95.55 ± 25.6 mg/kg. Highest content of free SA was found in EBN from Pontian district, Johor.