Effect of Polybutylene Succinate Additive in Polylactic Acid Blend Fibers via a Melt-Blown Process
2023
Benchamaporn Tangnorawich | Areerut Magmee | Nanjaporn Roungpaisan | Surachet Toommee | Yardnapar Parcharoen | Chiravoot Pechyen
This work aimed to study the influence of the polybutylene succinate (PBS) content on the physical, thermal, mechanical, and chemical properties of the obtained polylactic acid (PLA)/PBS composite fibers. PLA/PBS blend fibers were prepared by a simple melt-blown process capable of yielding nanofibers. Morphological analysis revealed that the fiber size was irregular and discontinuous in length. Including PBS affected the fiber size distribution, and the fibers had a smoother surface with increased amounts of added PBS. Differential scanning calorimetry analysis (DSC) revealed that the crystallization temperature of the PLA sheet (105.8 °:C) was decreased with increasing PBS addition levels down to 91.7 °:C at 10 wt.% PBS. This suggests that the addition of PBS may affect PLA crystallization, which is consistent with the X-ray diffraction analysis that revealed that the crystallinity of PLA (19.2%) was increased with increasing PBS addition up to 28.1% at 10 wt% PBS. Moreover, adding PBS increased the tensile properties while the % elongation at break was significantly decreased.
Show more [+] Less [-]AGROVOC Keywords
Bibliographic information
This bibliographic record has been provided by Multidisciplinary Digital Publishing Institute