CdS/CdSe quantum dots co-sensitized solar cells with Cu₂S counter electrode prepared by SILAR, spray pyrolysis and Zn–Cu alloy methods
2013
Salaramoli, Hosein | Maleki, Elham | Shariatinia, Zahra | Ranjbar, Maryam
Herein, CdS/CdSe co-sensitized TiO₂ photoanodes for QDSSCs were prepared by successive ionic layer adsorption and reaction (SILAR), spray pyrolysis and zinc–copper alloy processes. The HR-TEM, SEM, EDS, XRD, UV–vis and I–V curve analyses were performed to investigate the surface and structural properties of the prepared electrodes and the efficiencies of the fabricated QDSSs. Employing different methods for preparation of Cu₂S counter electrode affected the performance of QDSSCs under one illumination of sun (100mW/cm²) so that various conversion efficiencies (μ) of 3.18, 0.341 and 0.266% were measured in alloy, SILAR and spray pyrolysis methods, respectively. Therefore, among these methods, the zinc–copper alloy process with higher efficiency is preferred that gives fill factor (ff) and short circuit density (JSC) values of 0.44 and 11.69mA/cm². The HR-TEM images showed that CdS and CdSe QDs are in close contact with TiO₂ nanoparticles and the sizes of CdS and CdSe QDs are about 5 and 6nm, respectively. The energy-dispersive X-ray spectroscopy (EDS) measurement confirmed that CdS and CdSe QDs are successfully deposited on the surface of the TiO₂ film. The band gaps estimated from Tauc plots using UV–vis spectra vary from 3.1eV (without CdS and CdSe, bare TiO₂) to 2.38eV (TiO₂/CdS (3)/CdSe). The SEM images of Cu₂S counter electrodes prepared by zinc–copper alloy indicated nanosheets with high porosity that is much suitable for injection of electrolyte while in two other approaches (SILAR and spray pyrolysis), large (∼50–70nm) and small (∼10–17nm) nanoparticles were observed without high porosity.
Show more [+] Less [-]AGROVOC Keywords
Bibliographic information
This bibliographic record has been provided by National Agricultural Library