Synthesis of 2D MoS₂₍₁₋ₓ₎Se₂ₓ semiconductor alloy by chemical vapor deposition
2020
Yao, Wenwen | Kang, Zhilin | Deng, Jiajun | Chen, Yan | Song, Qian | Ding, Xun Lei | Lu, Fangchao | Wang, Wenjie
Alloying/doping in two-dimensional (2D) materials is emerging as an increasingly important strategy due to the wide-range bandgap tunability and versatility of these materials. Monolayer 2D transition metal dichalcogenide (TMD) alloy has been investigated both theoretically and experimentally in recent years. Here, we synthesized a bilayer MoS₂₍₁₋ₓ₎Se₂ₓ semiconductor alloy via the chemical-vapor deposition technique. The as-grown triangular MoS₂₍₁₋ₓ₎Se₂ₓ flakes with size of roughly 10 μm were observed by optical microscope and scanning electron microscope (SEM). The 1.4–1.9 nm thickness of the samples, as measured by AFM, means that bilayer MoS₂₍₁₋ₓ₎Se₂ₓ alloys were grown. The characteristic Raman modes related to Mo–S and Mo–Se vibrations were observed in the Raman spectrum. Two emission peaks were respectively found, corresponding to the A and B excitons in the photoluminescence (PL) spectrum. XPS measurements confirmed the Se doping of the alloy. The first-principles calculation results show a contraction of the band gap value with the increase of Se doping in the MoS₂ lattice. Compared with monolayer MoS₂₍₁₋ₓ₎Se₂ₓ alloy, the band bending effect is more obvious, and the bilayer MoS₂₍₁₋ₓ₎Se₂ₓ alloy still shows the direct band gap luminescence characteristic, which has certain guiding significance for the growth of two-dimensional materials and for device preparation.
Show more [+] Less [-]AGROVOC Keywords
Bibliographic information
This bibliographic record has been provided by National Agricultural Library