Effect of co-existing ions during the preparation of alumina by electrolysis with aluminum soluble electrodes: Structure and defluoridation activity of electro-synthesized adsorbents
2013
Tchomgui-Kamga, Eric | Audebrand, Nathalie | Darchen, André
The electrochemical dissolution of aluminum was carried out to prepare hydrated aluminas which were characterized by scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), X-ray diffraction (XRD), chemical titrations and defluoridation activities. Aluminas were obtained at controlled pH depending upon the counter cations of the electrolyte. A boehmite AlOOH phase was isolated mainly in ammonium solution, while aluminas synthesized in the other media contained a mixture of phases, usually both boehmite and bayerite γ-Al(OH)3. All the boehmite phases contained nano-crystallites of less than 3nm. Batch defluoridation experiments revealed a second influence of the original electrolyte. Aluminas were very effective in defluoridation with abatement rates of 99.5%, 98.5% and 97.3% from neutral fluoride solution at 10mgL−1 when they were prepared in solution of (NH4)2SO4, (NH4)HCO2 and NH4Cl, respectively. The maximum fluoride capacities were 46.94; 10.25 and 12.18mg g−1 for aluminas prepared in solution of (NH4)2SO4; (NH4)HCO2 and NH4Cl, respectively. The amount of dissolved Al was found to be less than 0.19mgL−1 at neutral pH. These results show that a defluoridation with electro-synthesized aluminas would be more efficient and safe than a direct electrocoagulation.
Show more [+] Less [-]AGROVOC Keywords
Bibliographic information
This bibliographic record has been provided by National Agricultural Library