The influence of positive pulses on HiPIMS deposition of hard DLC coatings
2019
Santiago Varela, José Antonio | Fernández Martinez, I. | Kozák, T. | Capek, J. | Wennberg, A. | Molina Aldareguía, Jon M. | Bellido González, V. | Gonzalez Arrabal, Raquel | Monclús, M. A.
Diamond-like Carbon (DLC) coatings were deposited by a novel HiPIMS method that incorporates positive voltage pulses at the end of the conventional HiPIMS discharge. Different positive voltage amplitudes (100, 200, 300, 400 and 500 V) were used to evaluate the effect of this operation mode on the discharge process and the mechanical properties of the deposited DLC coatings. The application of positive pulses was observed to enhance the ionization of both the sputtered carbon and argon species. Mass spectroscopy measurements showed that a larger amount of high-energy C+ ions are generated, with ion energies proportional to the amplitude of the overshoot voltage. The ion bombardment induced by the positive pulses led to higher compressive residual stresses and densification of deposited DLC coatings. Moreover, their Raman spectra exhibited lower D-band and G-band intensity ratios (ID/IG) as the pulses voltage was increased which is indicative of higher sp3 content. Mechanical properties were evaluated by nanoindentation testing and the hardness of the deposited DLC films was observed to increase from 9.6 GPa (for no voltage pulse applied) to 22.5 GPa (for an applied positive pulse voltage of 500 V).
Show more [+] Less [-]AGROVOC Keywords
Bibliographic information
This bibliographic record has been provided by Universidad Politécnica de Madrid