Adsorption of Cobalt(II) from Aqueous Solutions by Fe3O 4/Bentonite Nanocomposite
2015
Hashemian, Saeedeh | Ṣaffārī, Ḥusayn | Ragabion, Saeedeh
Fe₃O₄and Fe₃O₄/bentonite were prepared by chemical co-precipitation method. They were characterized by X-ray powder diffraction (XRD), Fourier infrared spectroscopy (FTIR), and transmission electron microscope (TEM). Adsorption of cobalt(II) on the bentonite, Fe₃O₄, and Fe₃O₄/bentonite nanocomposite was studied. The results indicated that the metal oxides mainly occurred in the form of spinel structure of Fe₃O₄and the presence of Fe₃O₄significantly affect the surface area and pore structure of the bentonite. The specific surface area (Brunauer–Emmett–Teller (BET) method) of bentonite, Fe₃O₄, and Fe₃O₄/bentonite were determined to be 34.44, 98.44, and 140.5 m² g⁻¹, respectively. TEM image of Fe₃O₄/bentonite shows the particle diameter at 10 nm. The maximum adsorption capacity of cobalt(II) by Fe₃O₄/bentonite nanocomposite was determined to be 18.76 mg g⁻¹. The adsorption strongly depends on pH, where the removal efficiency increases as the pH turns to alkaline range (pH 9). The results suggest that higher adsorption capacity of composite than bentonite is attributed to the presence of Fe₃O₄. The adsorption process follows pseudo-second-order kinetics. The equilibrium data was analyzed by Langmuir model showing high correlation coefficient. The thermodynamic study of adsorption process showed that the adsorption of Co(II) onto Fe₃O₄/bentonite was carried out spontaneously.
Show more [+] Less [-]AGROVOC Keywords
Bibliographic information
This bibliographic record has been provided by National Agricultural Library