Customization of surface wettability of nano-SiO2 by coating Trimethoxy(vinyl)silane modifier for oil-water separation: Fabrication of metal-based functional superwetting nanomaterial, characterizations and performance evaluation

The wettability of nano-SiO₂ surface was transformed from the inherent hydrophilicity to functional superhyderophobicity by coating Trimethoxy (vinyl)silane modifier, and the resultant surface showed contrasting wettability for water and oil (Superhydrophobic and Superoleophilic), which is a desired characteristic for the membranes used in oil-water separation. Initially Trimethoxy (vinyl)silane coated SiO₂ nanoparticles (TMVS@SiO₂) were synthesized by hydrolysis and poly-condensation reactions, and this nano dispersion was spray coated on the annealed stainless-steel mesh surface, whose resulting hierarchical surface texture brought about the desired wettability, with the water-surface-air (θWA) and oil-surface-air (θOA) interfacial contact angles of 150° and 0° respectively. In addition to the wettability studies (contact angles), FTIR, morphological, and elemental characterizations of the TMVS@SiO₂ coated surfaces were carried out to understand the alterations that have taken place on the TMVS@SiO₂ surface that in turn rendered superhydrophobicity and superoleophilicity to the surface. The FTIR absorption peaks indicate that after modifying SiO₂ with TMVS, the –OH groups on SiO₂ surface are clearly replaced by –CH₃. The morphological studies indicated that modification of SiO₂ leads to better cross-linking between coating composition and nanoparticles and EDS spectra and elemental mapping of the modified surface showed the presence of Si, O and C elements. Finally, this surface was tested for its efficiency and stability as a membrane in the process of separating oil and water from the oily water using gravity driven method. The oil-water separation efficiency was estimated to be 99% for this membrane and also it was found to be quite stable as the surface effectively retained this oil-water separation efficiency even after 10 cycles of separation process.