Synthesis of polyurea from 1,6-hexanediamine with CO2 through a two-step polymerization
2017
Shan Jiang | Ruhui Shi | Haiyang Cheng | Chao Zhang | Fengyu Zhao
Activation and transformation of CO2 is one of the important issues in the field of green and sustainable chemistry. Herein, CO2 as a carbon-oxygen resource was converted to CO2-polyurea with 1,6-hexanediamine through a two-step polymerization. The reaction parameters such as temperature, pressure and reaction time were examined; and several kinds of catalysts were screened in the absence and presence of NMP solvent. The formed oligomer and the final polyurea were characterized by FT-IR, VT-DRIFTS, NMR, XRD, AFM and their thermal properties were examined by TGA and DSC. It was confirmed that the final polyurea has a high thermal stability; the melting temperature is 269 °C and the decomposition temperature is above 300 °C. It is a brittle polymer with a tensile strength of 18.35 MPa at break length of 1.64%. The polyurea has a stronger solvent resistance due to the ordered hydrogen bond in structure. The average molecular weight should be enhanced in the post-polymerization as the appearance, hydrogen bond intensity, crystallinity, melting point and the thermal stability changed largely compared to the oligomer. The present work provides a new kind of polyurea, it is expected to have a wide application in the field of polymer materials. Keywords: CO2, Polyurea, Two-step polymerization, Catalysis
Mostrar más [+] Menos [-]Información bibliográfica
Este registro bibliográfico ha sido proporcionado por Directory of Open Access Journals