Carbon ion beam induced modifications of optical, structural and chemical properties in PADC and PET polymers

Kumar, Vijay; Sonkawade, R.G.; Chakarvarti, S.K.; Singh, Paramjit; Dhaliwal, A.S.

Carbon ion beam induced modifications of optical, structural and chemical properties in PADC and PET polymers

2012

Kumar, Vijay | Sonkawade, R.G. | Chakarvarti, S.K. | Singh, Paramjit | Dhaliwal, A.S.

We report a study on the carbon ion beam induced modifications on optical, structural and chemical properties of polyallyl diglycol carbonate (PADC) commercially named as CR-39 and Polyethyleneterepthalate (PET) polymer films. These films were then irradiated by 55MeV C⁵⁺ ion beam at various fluences ranging from 1×10¹¹ to 1×10¹³ ions/cm². The pristine as well as irradiated samples were subjected to UV–Visible spectral study (UV–Vis), Photoluminescence (PL), X-ray diffraction (XRD) and Fourier transform infrared (FTIR) spectroscopy. It has been found that ion irradiation may induce a sort of defects in the polymers due to chain scission and cross linking as observed from PL spectral study. It is revealed from UV–Vis spectra absorption edge shifted towards longer wavelength region after irradiation with increasing ion fluence. This shift clearly reflects decrease in optical band gap. The XRD study indicates the gradual decrease in intensity in case of PADC with increasing ion fluence. However, the intensity pattern increased in case of PET at fluence of 10¹¹ ion/cm² then decreased with further increase in fluence. Crystalline size of PADC was found to be decreasing gradually with increase of ion fluence. Whereas, the crystalline size of PET films found to increase with lower fluence and decreases with higher ion fluence. FTIR spectrum also shows the change in intensity of the typical bands after irradiation in the both the polymers. The results so obtained can be used successfully in heavy ions dosimetry using well reported techniques.

Afficher plus [+]