Polystyrene/decahydronaphthalene/propane phase equilibria and polymer conformation properties from intrinsic viscosities
2011
Cain, Nathaniel | Haywood, Alexander | Roberts, George | Kiserow, Douglas | Carbonell, Ruben
The influence of dissolved propane (up to 31.2 wt %) on the phase equilibria of 5 wt % polystyrene (PS) dissolved in 66/34 wt % trans/cis-decahydronaphthalene (DHN) was measured over the temperature range of 323-423 K. A suitable temperature, pressure, and propane composition operating space was defined to measure intrinsic viscosities of a single fluid phase. Intrinsic viscosities of PS in cosolvent mixtures of propane and trans/cis-DHN were measured between 323 and 423 K and between 70 and 208 bar. The addition of propane to the isomeric mixture of DHN resulted in a decreased solvent quality for PS, causing a contraction of the PS coil. The most dramatic decrease in solvent quality with the addition of propane occurred at 323 K and 70 bar with approximately a 36% reduction in the viscometric radius with the addition of 45 mol % propane to DHN. At 423 K, the solvent quality was less sensitive to the addition of propane and only a 13% reduction in the viscometric radius was observed at 70 bar and 45 mol % propane in DHN.
Afficher plus [+] Moins [-]Mots clés AGROVOC
Informations bibliographiques
Cette notice bibliographique a été fournie par National Agricultural Library
Découvrez la collection de ce fournisseur de données dans AGRIS