Biosorption of Methylene Blue from Aqueous Solutions by Hazelnut Shells: Equilibrium, Parameters and Isotherms
2008
Doğan, Mehmet | Abak, Harun | Alkan, Mahir
This paper presents a study on the batch adsorption of a basic dye, methylene blue (MB), from aqueous solution onto ground hazelnut shell in order to explore its potential use as a low-cost adsorbent for wastewater dye removal. A contact time of 24 h was required to reach equilibrium. Batch adsorption studies were carried out by varying initial dye concentration, initial pH value (3-9), ionic strength (0.0-0.1 mol L⁻¹), particle size (0-200 μm) and temperature (25-55°C). The extent of the MB removal increased with increasing in the solution pH, ionic strength and temperature but decreased with increase in the particle size. The equilibrium data were analysed using the Langmuir and Freundlich isotherms. The characteristic parameters for each isotherm were determined. By considering the experimental results and adsorption models applied in this study, it can be concluded that equilibrium data were represented well by Langmuir isotherm equation. The maximum adsorption capacities for MB were 2.14 x 10⁻⁴, 2.17 x 10⁻⁴, 2.20 x 10⁻⁴ and 2.31 x 10⁻⁴ mol g⁻¹ at temperature of 25, 35, 45 and 55°C, respectively. Adsorption heat revealed that the adsorption of MB is endothermic in nature. The results indicated that the MB strongly interacts with the hazelnut shell powder.
Afficher plus [+] Moins [-]Degradation of Hazardous Dyes in Wastewater using Nanometer Mixed Crystal TiO₂ Powders under Visible Light Irradiation
2008
Wang, Jun | Li, Ronghe | Zhang, Zhaohong | Sun, Wei | Wang, Xiaofang | Xu, Rui | Xing, Zhiqiang | Zhang, Xiangdong
The partial phase transformation of nanometer TiO₂ powder from anatase phase to rutile phase was realized by heat-treatment and a new TiO₂ photocatalyst which could be excited by visible light was obtained. The heat-treated TiO₂ powder at different stage of transition crystal was characterized and monitored by XRD, TEM, FT-IR and UV-vis DRS methods. The test of photocatalytic activity of the heat-treated TiO₂ powder was carried out by the photocatalytic degradation of rhodamine B and acid orange II dyes, respectively, in aqueous solution under visible light irradiation. The results indicate that the nanometer TiO₂ photocatalyst heat-treated at 500°C for 60 min shows the highest photocatalytic activity, that is, it can effectively degrade the rhodamine B and acid orange II under visible light irradiation. The remarkable improvement of photocatalytic activity of heat-treated TiO₂ powder at 500°C for 60 min was mainly illustrated by the formation of special interphase between rutile and anatase phases, which not only restrains the recombination of photogenerated electrons and holes, but also reduces the adsorbability of nanometer anatase TiO₂ powder properly for various dyes. Additionally, the effects of dye-assisting chemicals such as Na₂CO₃ and NaCl on the photocatalytic degradation were also studied.