Sr1–xCaxFeO3-δ as a New Oxygen Sorbent for the High-Temperature Pressure-Swing Adsorption Process
2016
Miura, Norio | Ikeda, Hiroshi | Tsuchida, Akinori
The low-cost and environmentally friendly perovskite-type oxide of Sr₁–ₓCaₓFeO₃₋δ was proposed here as a new oxygen sorbent usable in a high-temperature pressure-swing adsorption (HT-PSA) process for oxygen production (separation) from air. The oxygen sorption/desorption properties of the Sr₁–ₓCaₓFeO₃₋δ samples (x = 0–1.0) were examined at 550 °C by means of thermogravimetric analysis (TGA). Among the examined samples, Sr₀.₇₆Ca₀.₂₄FeO₃₋δ (x = 0.24) was found to exhibit the largest value (7.8 cm³ g–¹) for the amount of reversibly sorbed/desorbed oxygen by the change in oxygen concentration between air (21 vol % O₂) and 5 vol % O₂. For such an excellent oxygen sorption/desorption behavior to be verified, the oxygen content (oxygen nonstoichiometry, 3-δ) in Sr₀.₇₆Ca₀.₂₄FeO₃₋δ was estimated as a function of ambient oxygen concentration. The oxygen content of Sr₀.₇₆Ca₀.₂₄FeO₃₋δ was sensitive to the oxygen concentration and varied largely with its change, especially in the range of 5–21 vol % O₂. Thus, it is expected that the large change in oxygen content can result in the large amount of reversibly sorbed/desorbed oxygen even by a small pressure-swing amplitude. Actually, the Sr₀.₇₆Ca₀.₂₄FeO₃₋δ pellet sample was evaluated as an oxygen sorbent for the HT-PSA process by using a small-column apparatus. As a result, the amount of oxygen production for the Sr₀.₇₆Ca₀.₂₄FeO₃₋δ pellet sample indicated 4.9 cm³ g–¹ per cycle at 600 °C. This value was approximately two times larger than that for the benchmark sample of La₀.₁Sr₀.₉Co₀.₉Fe₀.₁O₃₋δ (LSCF1991).
Показать больше [+] Меньше [-]Ключевые слова АГРОВОК
Библиографическая информация
Эту запись предоставил National Agricultural Library