Physical and mechanical properties of three-layer wood composites made from bamboo and rice straw
2006
Salim Hiziroglu | Songklod Jarusombuti | Piyawade Bauchongkol | Vallayuth Fueangvivat | Worakit Soontonbura
This study evaluated some of the important properties of three-layer particleboard panels made from bamboo (Dendrocalamus asper) and rice straw. A total of twenty experimental panels with average target density levels of 0.65 g/cm and 0.75g/cm were made from the mixture of 95% bamboo and 5% rice straw particles. Modulus of elasticity (MOE), modulus of rupture (MOR), internal bond strength (IB), thickness swelling (TS), density profiles, and surface roughness of the specimens were determined. Samples with 0.75g/cm density had 34 percent and 27 percent higher MOE and MOR values than those of samples with target density of 0.65g/cm, respectively. It appears that using 5% of rice straw in the panels did not significantly reduce both physical and mechanical properties of the samples. The panels made in this study satisfied strength requirements for general uses based on Japanese Standard. Measurement of surface characteristics of the samples resulted that such panels can be used as substrate for thin overlays without any significant problems. Initial findings of this study suggest that both non-wood under-utilized species can be considered as raw material manufacture value-added three-layer particleboard panels.
显示更多 [+] 显示较少 [-]