Preparation and thermal stability evaluation of cellulose nanofibrils from bagasse pulp with differing hemicelluloses contents
2020
Lu, Yanxu | Tao, Peng | Zhang, Ni | Nie, Shuangxi
In this work, cellulose nanofibrils (CNFs) are produced from bagasse pulps with differing hemicelluloses contents by ultrafine grinding and high-pressure homogenization. The results showed that hemicelluloses content in the range of 9.7–21.7 wt.% led to nanofibrils with average diameter. A decrease in hemicelluloses content can enhance the crystallinity and improve the thermal stability of the CNFs. The activation energy of the CNF samples with hemicelluloses contents of 9.7 wt.%, 12.72 wt.%, 15.7 wt.%, 18.76 wt.%, and 21.7 wt.% are 713.03, 518.93, 462.62, 421.78, and 211.11 kJ/mol, respectively, when the conversion rate is increased from 30%–90%. These results demonstrate that hemicelluloses content has a considerable influence on the properties of CNFs. This work provides a theoretical basis for high-value utilization of CNFs, and enriches useful information on the application of CNF materials.
显示更多 [+] 显示较少 [-]