Defluoridation Performance Comparison of Nano-hydrotalcite/Hydroxyapatite Composite with Calcined Hydrotalcite and Hydroxyapatite
2016
Sani, Taju | Adem, Mohammedali | Fetter, Geolar | Bosch, Pedro | Diaz, Isabel
Fluoride retention from water is nowadays a serious health problem. This study reports the potential of a newly developed nano-hydrotalcite/hydroxyapatite (n-HT/HAp) composite, and its constituent materials, hydrotalcite (HT) and hydroxyapatite (HAp), in fluoride removal. Calcined hydrotalcites (cHT) showed a remarkable fluoride removal ability from water through memory effect mechanism. HAp, the mineral compound of bones, adsorbs fluoride as well but through ion exchange mechanism. Fluoride substitutes hydroxyls to produce fluorapatite. Among the tested calcined hydrotalcites, cHT Mg-Al (4:1) sample, composed of magnesium divalent cation to aluminum ratio of 4, was identified as the best-performing hydrotalcite. The differences among cHT samples in fluoride removal capacities are attributed to hydrotalcite composition as well as to particle size. The performance of these materials is compared with that of n-HT/HAp composite whose main features are basic acidic material and not yet tested in fluoride retention. Interestingly, n-HT/HAp also performs best, 98 %, slightly higher than the best cHT Mg-Al (4:1) sample with 97 % fluoride removal efficiency from such a high initial fluoride solution of 20 mg/L at 10 g/L dose, yielding the final residual fluoride concentrations of 0.36 and 0.6 mg/L, respectively; both meet the WHO standard for drinking water. Besides, the uncalcined hydrotalcite constituent added virtue to the advantage of using n-HT/HAp in fluoride removal as the efficiency was compensated by the nanometric size of the hydrotalcite particle.
显示更多 [+] 显示较少 [-]