Thermoelectric performance of SnS and SnS–SnSe solid solution
2015
Han, Ye-Mao | Zhao, Jie | Zhou, Min | Jiang, Xing-Xing | Leng, Hua-Qian | Li, Lai-Feng
Solid solution is a potential way to optimize thermoelectric performance for its low thermal conductivity compared to those of the constituent compounds because of the phonon scattering from disordered atoms. Tin(ii) sulfide (SnS) shows analogous band structure and electrical properties with tin selenide (SnSe), which was the motivation for investigating the thermoelectric performance of SnS and SnS–SnSe solid solution system. SnS compound and SnS₁₋ₓSeₓ (0 < x < 1) solid solution were fabricated using the melting method and they exhibited anisotropic thermoelectric performance along the parallel and perpendicular to the pressing directions. For the SnS compound, the maximum zT∥ value is 0.19 at 823 K along the parallel to pressing direction, which is higher than that along the perpendicular to the pressing direction (zT⊥ = 0.16). The zT values of SnS₀.₅Se₀.₅ and SnS₀.₂Se₀.₈ were higher than those of the SnS compound and a maximum zT value of 0.82 was obtained for SnS₀.₂Se₀.₈ at 823 K, which is more than four times higher than that of SnS.
显示更多 [+] 显示较少 [-]