Surface modification of graphene and graphite by nitrogen plasma: Determination of chemical state alterations and assignments by quantitative X-ray photoelectron spectroscopy
2015
Bertóti, Imre | Mohai, Miklós | László, Krisztina
Multilayer graphene (MLGR) and its bulk analog, highly oriented pyrolytic graphite (HOPG), were treated by radio frequency activated low pressure N2 gas plasma (at negative bias 0–200V, for 5–20min). Surface composition and chemical-state alterations were delineated by X-ray photoelectron spectroscopy (XPS). Covalently bonded nitrogen of 5–15at% incorporated into the surface. The higher N concentration in MLGR below 100V is attributed to the larger number of defects. The equal N content at 200V indicates intensive formation of reactive sites. In-depth distribution of N is restricted to 2–4 monolayers. Model calculation resulted in 23at% N (at 100V) in the top graphene layers of HOPG. Three different chemical states of nitrogen (pyridine-type at 398.3eV, pyrrole- and triazine-type at 399.7eV and N substituting C in graphite-like network at 400.9eV) were determined from high-resolution N1s spectral region for all samples. Pyridine and pyrrole–triazine components increase preferentially with increasing bias. Alterations of the C1s and O1s spectra are discussed in a critical approach. The amount of reacted carbon was consistent with that required for the three different nitrogen and oxygen states, thus validating the proposed assignments.
显示更多 [+] 显示较少 [-]