Comparison of hydroxyapatite-coated and uncoated pins for transfixation casting in horses
2012
Lescun, Timothy B. | Baird, Debra K. | Oliver, Laurinda J. | Adams, Stephen B. | Hawkins, Jan F. | Moore, George E.
Objective: To determine the extent to which a hydroxyapatite coating promotes pin stability in the third metacarpal bone during transfixation casting in horses. Animals: 14 adult horses. Procedures: 7 horses each were assigned to either an uncoated or hydroxyapatite-coated pin group. Three transcortical pins were placed in the third metacarpal bone of each horse and incorporated into a cast for 8 weeks. Insertion and extraction torque were measured, and torque reduction was calculated. Radiography was performed at 0, 4, and 8 weeks. Lameness evaluation was performed at 2, 4, 6, and 8 weeks. Bacteriologic culture of pins and pin holes was performed at pin removal. Results: All horses used casts without major complication throughout the study. Insertion torque was higher in uncoated pins. There was no effect of group on extraction torque. Hydroxyapatite-coated pins had lower torque reduction. Five of 15 hydroxyapatite-coated pins maintained or increased stability, whereas all uncoated pins loosened. Pin hole radiolucency, lameness grades, and positive bacteriologic culture rates were not different between groups. Conclusions and Clinical Relevance: Hydroxyapatite coating increased pin stability within the third metacarpal bone of horses during 8 weeks of transfixation casting but did not improve pin performance on clinical assessments. Clinical use of hydroxyapatite-coated transfixation pins may result in greater pin stability; however, further research is necessary to improve the consistency of pin osteointegration and elucidate whether clinical benefits will ultimately result from this approach in horses.
显示更多 [+] 显示较少 [-]