Nitrogen-Enriched Porous Carbon Fiber as a CO₂ Adsorbent with Superior CO₂ Selectivity by Air Activation
2019
Xiong, Long | Wang, Xue-Fei | Li, Li | Jin, Lu | Zhang, Yong-Gang | Song, Shu-Lin | Liu, Rong-Pei
Nitrogen-enriched porous carbon fibers were successfully prepared by one-step carbonization–activation treatment of oxidized polyacrylonitrile fibers. Utilizing the low-temperature carbonization and air activation, lots of narrow micropores were developed, and the volume of pores with a size below 0.8 nm was in the range of 0.110–0.122 g/cm³. Meanwhile, nitrogen preserved in the fibers exceeded 20.8 wt % in content. The porous carbon fiber exhibited an optimal CO₂ uptake of 99 mg/g at 25 °C and 1 bar. More importantly, an incomparable Henry’s law CO₂/N₂ selectivity of 183 was achieved, which was primarily attributed to the prominent nitrogen-containing functionalities. Additionally, the sample had a low isosteric heat of adsorption, between 26.65 and 30.84 kJ/mol. This work provides a convenient strategy for the construction of CO₂ adsorbent with high selectivity from nitrogen-containing starting materials.
显示更多 [+] 显示较少 [-]