Enhanced photoelectrocatalytic activity for dye degradation by graphene–titania composite film electrodes
2012
Wang, Peifang | Ao, Yanhui | Wang, Chao | Hou, Jun | Qian, Jin
Graphene–titania composite film electrodes have been fabricated by a dip-coating method. Transmission electron microscopy (TEM) images show that the titania nanoparticles were dispersed uniformly, with only a little aggregation on the surface and edges of the graphene sheets. XRD analysis showed that the composite electrodes comprised the anatase phase of titania with just a little rutile phase. The photoelectrocatalytic activities of the as-prepared samples were investigated by studies of the degradation of Reactive Brilliant Red dye X-3B (C.I. reactive red 2). An enhancement of the photocurrents was observed using the graphene–titania composite electrodes, compared with pure titania film electrodes, under UV light irradiation. This improvement is attributed to the following two reasons: enhanced migration efficiency of the photo-induced electrons and enhanced adsorption activity of the dye molecules. In addition, we investigated the effects of graphene content and pH values on the photoelectrocatalytic activity of the as-prepared composite film electrodes. Results showed that there was an optimal amount of 5% (initial graphite oxide content).
显示更多 [+] 显示较少 [-]