Improved coulombic efficiency and cycleability of SnO₂–Cu–graphite composite anode with dual scale embedding structure
2016
Lü, Bin | Hu, Renzong | Liu, Jiangwen | Liu, Jun | Wang, Hui | Zhu, Min
To improve the coulombic efficiency (CE) and cycle life of SnO₂ anode in lithium ion batteries, SnO₂–Cu–graphite composites with dual scale embedding structure are synthesized by ball milling. The SnO₂–Cu composite, in which SnO₂ nanoparticles with grain size less than 10 nm are uniformly dispersed in inactive nanocrystalline Cu matrix, is firstly obtained by milling the mixture of SnO₂ and Cu nanopowders (molar ratio 1 : 2), and then further milling with graphite (C) to obtain SnO₂–Cu–C composite with microsized graphite sheets as matrix of SnO₂–Cu composite. The 50 h-milled SnO₂–Cu composite exhibits higher initial CE (76.0 ± 1.5%) and subsequent CE than 50 h-milled SnO₂. Furthermore, the SnO₂–Cu–C composite anode is capable of retaining a maximum charge capacity of 450.8 mA h g⁻¹ at 100 mA g⁻¹ after 80 cycles with a capacity retention ratio of 74.4%, displaying superior cyclic stability to as-milled SnO₂, SnO₂–Cu and SnO₂–C composites. The improved CE and cycleability are attributed to the unique dual scale embedding structure that offers good conductivity of electron and lithium ion as well as the nanostructure stability of active materials. This unique composite structure might be extended to other high-capacity anode materials, to achieve high performance lithium ion batteries.
显示更多 [+] 显示较少 [-]