A facile method to prepare translucent anatase thin films in monolithic structures for gas stream purification
2018
Rodrigues-Silva, Caio | Monteiro, Ricardo A. R. | Dezotti, Márcia | Silva, Adrián M. T. | Pinto, Eugénia | Boaventura, Rui A. R. | Vilar, Vítor J. P.
In the present work, a facile method to prepare translucent anatase thin films on cellulose acetate monolithic (CAM) structures was developed. A simple sol–gel method was applied to synthesize photoactive TiO₂ anatase nanoparticles using tetra-n-butyl titanium as precursor. The immobilization of the photocatalyst on CAM structures was performed by a simple dip-coating method. The translucent anatase thin films allow the UV light penetration through the CAM internal walls. The photocatalytic activity was tested on the degradation of n-decane (model volatile organic compound—VOC) in gas phase, using a tubular lab-scale (irradiated by simulated solar light) and pilot-scale (irradiated by natural solar light or UVA light) reactors packed with TiO₂-CAM structures, both equipped with compound parabolic collectors (CPCs). The efficiency of the photocatalytic oxidation (PCO) process in the degradation of n-decane molecules was studied at different operating conditions at lab-scale, such as catalytic bed size (40–160 cm), TiO₂ film thickness (0.435–0.869 μm), feed flow rate (75–300 cm³ min⁻¹), n-decane feed concentration (44–194 ppm), humidity (3 and 40%), oxygen concentration (0 and 21%), and incident UV irradiance (18.9, 29.1, and 38.4 WUV m⁻²). The decontamination of a bioaerosol stream was also evaluated by the PCO process, using Pseudomonas aeruginosa (Gram-negative) and Staphylococcus aureus (Gram-positive) as model bacteria. A pilot-scale unit was operated day and night, using natural sunlight and artificial UV light, to show its performance in the mineralization of n-decane air streams under real outdoor conditions. Graphical abstract Normally graphics abstract are not presented with captions/legend. The diagram is a collection of images that resume the work
显示更多 [+] 显示较少 [-]