Synthesis and characterization of a novel polymer based on anthracene moiety for organic thin film transistor
2008
Li, Yinam | Kim, Tae-Hoon | Zhao, Qinghua | Kim, Euh-Kyung | Han, Seung-Hon | Kim, Yun-Hi | Jang, Jin | Kwon, Soon-Ki
We have designed and synthesized a new polymer, which could be used in the organic thin film transistor (OTFT). Poly[2,6-bis(3'-dodecythiophene-2'-yl)anthracene] (PDTAn), which is composed with anthracene moiety and dodecyl alkyl thiophene, was synthesized by oxidative polymerization using iron (III) chloride. The mole ratio of FeCl₃ and monomer (4.2:1), keeping low temperature during the initiation reaction, amount of solvent, and dropping order were very important for oxidative polymerization without crosslinking. The molecular weight of the polymer (Mw) was measured to be 40,000 with 2.85 of polydispersity index by GPC. The physical and optical properties of the polymer were characterized by differential scanning calorimetry (DSC), cyclic voltammetry (CV), and optical absorption and photoluminescence (PL) spectroscopy. A field-effect mobility of 1.1 x 10⁻⁴ cm² V⁻¹ S⁻¹, a current on/off ratio of 10⁵, and the Vth at -15.2 V had been obtained for OTFTs using this polymer semiconductor by solution coating.
显示更多 [+] 显示较少 [-]