Synthesis of APTMS-Functionalized SiO₂/TiO₂ Transparent Film Using Peroxo Titanic Acid Refluxed Solution for Formaldehyde Removal
2010
Photong, Somjate | Boonamnuayvitaya, Virote
Amine-functionalized SiO₂/TiO₂ photocatalytic films have been synthesized using the peroxo titanic acid (PTA) approach coupled with the sol-gel dip-coating method. The 3-aminopropyl-trimethoxysilane (APTMS) and methyltrimethoxysilane (MTMOS) were employed as the amine functional groups and silica precursor. The effects of the ratio of APTMS/MTMOS, PTA refluxed time, and pH of prepared sol on the characteristics and the formaldehyde degradation efficiency were investigated. Physicochemical properties of prepared photocatalysts were characterized with nitrogen adsorption-desorption isotherm measurement, SEM, X-ray diffraction (XRD), UV-vis spectrophotometer, and Fourier transform infrared (FTIR) spectroscopy. The XRD and FTIR results indicated that the obtained photocatalysts consisted of -NH₂ groups, SiO₂, and anatase TiO₂. The photocatalytic films showed high transmittance of 80-90% in the visible light region. The obtained film prepared with the APTMS/MTMOS ratio of 0.03, pH of 1.8, and 10 h of refluxed time possessed high specific surface area (604.0 m² g⁻¹) and 85% formaldehyde degradation efficiency. The enhancement of formaldehyde degradation efficiency was observed when increasing the PTA refluxed time. The repeatability of photocatalytic film was also tested, and the degradation efficiency was 92.0% of initial efficiency after seven cycles.
显示更多 [+] 显示较少 [-]