Desorption of bis(2-chloroethyl) sulfide, mustard agent, from the surface of hardened cement paste (HCP) wafers
2013
Tang, Hairong | Zhou, Xuezhi | Guan, Yingqiang | Zhou, Liming | Wang, Xinming | Yan, Huijuan
The decontamination of surfaces exposed to chemical warfare agents is an interesting scientific topic. The desorption behavior of bis(2-chloroethyl) sulfide (sulfur mustard, HD) from the surface of the HD-contaminated hardened cement paste (HCP) was investigated under different weather conditions, which should provide scientific reference data for protection and decontamination projects involving HD-contaminated HCP in different conditions. The desorption of HD from the surface of HCP wafers was studied, and the effects of the purge air flow rate, water content, sorption temperature, and substrate age were investigated. HD desorption was detected from the surface of HD-contaminated HCP, but the desorption velocity was relatively slow. The desorption quantity remained within an order of magnitude throughout a time span of 36h (25°C at 200mL/min of purge air), and the amount of HD that was desorbed from each square meter of HCP surface was approximately 1.1g (25°C at 200mL/min of purge air), which was approximately 5.5 percent of the total HD that was initially applied. A higher flow rate of the purge air, increased water content, and longer substrate age of HCP all increased the HD desorption. In contrast, increased temperatures suppressed HD desorption.
显示更多 [+] 显示较少 [-]