Catalytic Degradation of Humic Acid by Mn-Cu/Al-MCM-41 Catalyst in Electro-Fenton/Chlorine Processes: Influencing Factors, Mechanisms, and Kinetics
2019
Liu, Zailiang | Meng, Hailing | Li, Chao | Liu, Tinglei | Cao, Jiashun | Lv, Yaohui
Degradation of humic acid (HA) in heterogeneous electro-Fenton/chlorine processes was investigated using a catalyst of Mn-Cu bimetallic oxides supported on Al-containing MCM-41. The catalyst was synthesized by co-precipitation method and characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), N₂ adsorption–desorption, and X-ray photoelectron spectroscopy (XPS) techniques. The bimetallic oxide catalyst exhibited a higher activity compared to monometallic one. Adding Al in the bimetallic oxide catalyst enhanced the stability of the catalyst, reduced metal ion leaching, increased the initial ratio of Mn³⁺/Mn⁴⁺ and Cu⁺/Cu²⁺, and slightly enhanced the degradation efficiency of HA and corresponding chemical oxygen demand (COD). The effect of Mn and Cu content in MCM-41, catalyst dosage, pH value, and initial concentration of HA and salinity on degradation efficiency were investigated. A high COD reduction about 91.5% and general current efficiency (GCE) about 41.7% have been achieved under the optimal conditions of pH 6, salinity 1000 mg/L, catalyst dosage 0.5 g/L, HA sodium salt concentration 200 mg/L, and reaction time 60 min. A possible mechanism for the reaction was suggested. Kinetic analysis showed that HA degradation in the electro-Fenton/chlorine processes was fit with first-order kinetics.
显示更多 [+] 显示较少 [-]