Hierarchical hollow-tubular porous carbon microtubes prepared via a mild method for supercapacitor electrode materials with high volumetric capacitance
2022
Xiao, Xuan | Song, Lei | Wang, Qianli | Wang, Zhicheng | Wang, Hongyan | Chu, Juncai | Liu, Jianmin | Liu, Xinru | Bian, Zhentao | Zhao, Xuanxuan
In this paper, hollow-tubular porous carbons were synthesized from abundant biomass Cycas fluff (CF) through simple carbonization followed by an NaHCO₃ mild activation process. After activation, the tubular structure of the CF was retained, and a hierarchical structure of micropores, mesopores and macropores was formed. When the optimal mass ratio of NaHCO₃/CF is 2, the obtained porous carbon CF-HPC-2 sample has a large specific surface area (SSA) of 516.70 m² g⁻¹ in Brunauer–Emmett–Teller (BET) tests and a total pore volume of 0.33 cm³ g⁻¹. The C, O, N and S contents of CF-HPC-2 were tested as 91.77 at%, 4.09 at%, 3.54 at%, and 0.6 at%, respectively, by elemental analysis. Remarkably, CF-HPC-2 exhibits a high volume capacitance (349.1 F cm⁻³ at 1 A g⁻¹) as well as a higher rate capability than other biomass carbon materials (289.1 F cm⁻³ at 10 A g⁻¹). Additionally, the energy density of the CF-HPC-2 based symmetric supercapacitor in 2 M Na₂SO₄ electrolyte at 20 kW kg⁻¹ is 27.72 W h kg⁻¹. The particular hollow tubular morphology and activated porous structure determine the excellent electrochemical performance of the material. Hence, this synthetic method provides a new way of storing energy for porous carbon as high volumetric capacitance supercapacitor materials.
显示更多 [+] 显示较少 [-]