Origin of the double melting peaks of poly(3‐hydroxybutyrate‐co‐3‐hydroxyvalerate) with a high HV content as revealed by in situ synchrotron WAXD/SAXS analyses
2019
Zhu, Hao | Lv, You | Shi, Dan | Li, Yiguo | Wang, Zongbao
We here reported the dual melting behaviors with a large temperature difference more than 50 °C without discernible recrystallization endothermic peak in isomorphous poly(3‐hydroxybutyrate‐co‐3‐hydroxyvalerate) (P(HB‐co‐HV)) with a high HV content of 36.2 mol %, and the structure evolution upon heating was monitored by in situ synchrotron wide‐angle X‐ray diffraction/small‐angle X‐ray scattering (WAXD/SAXS) to unveil the essence of such double endothermic phenomena. It illustrated that the thinner lamellae with the larger unit cell and the thicker crystals having the smaller unit cell were melted around the first low and second high melting ranges, respectively. By analyzing in situ WAXD/SAXS data, and then coupling the features of melting behavior, the evolution of the parameters of both crystal unit cell and lamellar crystals, we proposed that the thinner unstable lamellae possess a uniform structure with HV units total inclusion, and the thicker stable lamellae reflect the sandwich structure with HV units partial inclusion. It further affirmed that the thicker sandwich and thinner uniform lamellae formed during the cooling and subsequent isothermal crystallization processes, respectively. These findings fully verify that it is the change of structure of lamellae rather than the melting/recrystallization that is responsible for double melting peaks of isomorphous P(HB‐co‐36.2%HV), and enhance our understanding upon multiple endothermic behaviors of polymers. © 2019 Wiley Periodicals, Inc. J. Polym. Sci., Part B: Polym. Phys. 2019, 57, 1453–1461
显示更多 [+] 显示较少 [-]