Analyses of Corrosion Potential from Inhibitor-Admixed Steel-Reinforced Concrete: Implication on Steel-Rebar Corrosion Risk/Probability
2015
Olugbenga, Adeshola Omotosho | Okeniyi, Joshua Olusegun | Ajayi, O. O. | Ajanaku, K. O. | Loto, C. A. | Popoola, Abimbola Patricia Idowu
Statistical analyses of three probability density functions, from Normal, Rayleigh and Weibull distributions, were applied for studying steel-rebar corrosion risk/probability in inhibitor admixed steel-reinforced concrete immersed in aggressive media of 3.0% NaCl and 0.5 M H2SO4. For these, different concentrations, ranging from 0 M to 0.29 M, of K2CrO4 were admixed in two-set steel-reinforced concrete with each set partially immersed in each of the aggressive test-solutions and which were monitored using open circuit potential techniques as per ASTM C876–91 R99. Analyses of the 30-days test-response from these showed that most of the corrosion test-data distributed like the Weibull and like the Normal distributions while just a few test-datasets distributed like the Rayleigh distribution, according to the Kolmogorov-Smirnov goodness-of-fit statistics. All the probability distribution fittings identified, in agreements, the 0.15 M K2CrO4 admixed steel-reinforced concrete with the least probability of corrosion risk in both of the acidic and the neutral saline test-solutions. These bear implications on the use of probability distribution analyses for economical monitoring of steel-rebar corrosion risk/probability and corrosion inhibitor admixture effects in steel-reinforced concrete in aggressive service-environments.
显示更多 [+] 显示较少 [-]