Investigation on mechanical properties of HDPE recycled composite filled by furfural residue produced from bagasse
2015
Hossein Ahmadi | Amir hooman hemmasi | Saeed Mahdavi
The aim of this study is investigating the mechanical properties of recycled HDPE (high-density polyethylene) filled by furfural residue produced from bagasse. For this purpose, rHDPE was used at three levels 58, 68 and 78% and furfural residue as a filler was added at levels of 20, 30 and 40%. The grafted maleic anhydride with polyethylene (PE-g-MA) was used at constant amount of 2% as compatibilizer which prepared from Arya polymer Co. The ingredients mixed in two screw extruder and test samples were made using injection molding method. Composite properties such as tensile strength, flexural and V-notch impact were measured according to ASTM standards. The results showed that with increasing the filler content of 20 and 30% by weight, tensile modulus and flexural strength increased compared to the control and then reduced by 40 percent of filler. FTIR spectroscopy of the furfural residue and composite filled by 30% was carried out. Also, by increasing the filler content of 20 to 40% by weight, V-notch impact strength of composite decreased. FTIR spectroscopy revealed that the absorption bands of carbonyl groups (C=O) in 1750-1600 cm-1 wavelength has slightly increased in the present of maleic anhydride compatibilizer which resulted maximum increasing of mechanical properties of composite using 30% residual furfural.
显示更多 [+] 显示较少 [-]