Experimental Study on Mechanical Properties of Paste Backfill with Flue-Gas Desulphurisation Gypsum under Combined Action of Dry–Wet Cycles and Chloride Erosion
2021
Sheng Wang | Feng Wang | Dawei Yin | Tianqi Jiang | Zhen Zhang
Flue-gas desulphurisation gypsum—a solid waste from power plants—can be used to prepare paste backfill for reducing costs. Most paste backfills are exposed to dry–wet cycles and chloride salt-rich water in mines. Therefore, the mechanical properties and damage mechanisms of paste backfill with desulphurised gypsum under the coupling action of erosion due to chloride with different concentrations and dry–wet cycles were investigated using methods such as visual observation, mass measurement, uniaxial compression, acoustic emission, Fourier-transform infrared spectroscopy, X-ray diffraction analysis, and field-emission scanning electron microscopy. With an increasing number of dry–wet cycles, the mass, elastic modulus, and strength of the paste backfill exhibited the trend of increasing first and then decreasing. The failure mechanism changed from mainly vertical fractures to the alternating development of vertical and horizontal fractures. The surface denudation effect of the specimens in a solution with a higher concentration was more severe under the same number of dry–wet cycles. In this study, the laws governing the mass change, strength change, degree of surface denudation, and failure pattern of desulphurised gypsum-filled specimens under different concentrations of chloride salt and different numbers of dry–wet cycles were derived.
显示更多 [+] 显示较少 [-]