Effect of Fe2O3 Content and Acid on the Leaching Behavior of Phosphorus from Dephosphorization Slag
2021
Shi-Wei Liu | Ping-Ping Li | Chuan-Ming Du | Ning-Ning Lv
Dephosphorization slag contains considerable quantities of valuable components, such as P2O5 and FeOx. To recover P from dephosphorization slag, selective leaching has been adopted to separate the P-concentrating mineral phase. In this study, the effect of Fe2O3 content in slag and acid on the leaching behavior of P from dephosphorization slag was investigated. It was found that a higher Fe2O3 content in slag resulted in a higher P2O5 content in the C2S–C3P solid solution. Increasing the Fe2O3 content in slag promoted the dissolution of P and simultaneously suppressed the dissolution of other elements, facilitating the selective leaching of P. In the hydrochloric acid solution, more than 81% of P could be dissolved from dephosphorization slag at pH 4, and the dissolution ratio of Fe was nearly zero, achieving excellent selective leaching. Although better selective leaching was also realized in the citric acid solution at pH 5, hydrochloric acid was considered the appropriate leaching agent from the perspective of leaching cost. Through selective leaching, almost all the C2S–C3P solid solution was dissolved from dephosphorization slag, and the Fe-bearing matrix phase and magnesioferrite remained in the residue. The residue with low P2O5 content can be reutilized in ironmaking or steelmaking processes.
显示更多 [+] 显示较少 [-]