Biodegradable Film of Starch-Based Carboxymethyl Cellulose from Rice Husk and Straw for Application in Food Preservation
2025
Worapan Pormsila | Phinyo Udomphoch
This study investigated the conversion of cellulose from rice husk (RH) and straw (RS), two types of agricultural waste, into Carboxymethyl cellulose (CMC). Cellulose was extracted using KOH and NaOH, hydrolyzed, and bleached to increase purity and fineness. The cellulose synthesis yielded a higher net CMC content for RH-CMC (84.8%) than for RS-CMC (57.7%). Due to smaller particle sizes, RH-CMC exhibited lower NaCl content (0.77%) and higher purity. FT-IR analysis confirmed similar functional groups to commercial CMC, while XRD analysis presented a more amorphous structure and a higher degree of carboxymethylation. A biodegradable film preparation of starch-based CMC using citric acid as a crosslinking agent shows food packaging properties. The biodegradable film demonstrated good swelling, water solubility, and moisture content, with desirable mechanical properties, maximum load (6.54 N), tensile strength (670.52 kN/m2), elongation at break (13.3%), and elastic modulus (2679 kN/m2), indicating durability and flexibility. The RH-CMC film showed better chemical and mechanical properties and complete biodegradability in soil within ten days. Applying the biodegradable film for tomato preservation showed that wrapping with the film reduced weight loss more efficiently than dip coating. The additional highlight of the work was a consumer survey in Thailand that revealed low awareness but significant interest in switching to alternative uses, indicating commercial potential for eco-friendly packaging choices and market opportunities for sustainable materials.
显示更多 [+] 显示较少 [-]