Preparation and characterization of zeolite type 4A using Kaolin from Ajebo, Nigeria
2019
Ovri, Henry | Ekpe, Ikenna Christopher | Chaudhary, Anna-Lisa | Mgbemere, Henry Ekene | Lawal, Ganiyu
This work investigates the hydrothermal synthesis and characterization of zeolite-4A from kaolin found in Ajebo, Nigeria calcined at 700 and 900°C respectively. The synthesized zeolite-4A was further characterised using X-ray Fluorescence (XRF), Fourier Transform Infrared spectrometer (FTIR), Scanning Electron Microscopy (SEM), X-Ray diffraction (XRD), Brunauer-Emmet-Teller (BET) surface area analysis as well as Differential Thermal Analysis/Thermo-gravimetric (TG). Water adsorption capacity tests were also carried out on the synthesized zeolite-4A. The results from the XRF measurements indicated that the amount of Al₂Oз and SiO₂ in the studied kaolin was similar to the standard kaolin composition making it a perfect candidate for zeolite-4A synthesis. FTIR showed the characteristic zeolite peaks while XRD confirmed the crystalline nature of the synthesized zeolite-4A. TG studies showed that the zeolite-4A samples were stable up to temperatures of 700°C. This stability as well as the surface area and pore size of 7 Å makes it potentially suitable for use in water treatment applications. The SEM showed cubic crystals which were typical of the morphology of zeolite-4A with water adsorption capacity of approximately 29%. These results indicate that zeolite4A can be synthesized from kaolin found in Ajebo as an inexpensive alternative to traditionally sourced materials and also is suitable for use as adsorption agent.
Mostrar más [+] Menos [-]Palabras clave de AGROVOC
Información bibliográfica
Este registro bibliográfico ha sido proporcionado por Universiti Putra Malaysia