A novel flame-retardant composite material based on calcium alginate/poly (vinyl alcohol)/graphite hydrogel: thermal kinetics, combustion behavior and thermal insulation performance

Liu, Jinru; Yu, Zhicai; He, Hualing; Wang, Yushu; Zhao, Yuhang

A novel flame-retardant composite material based on calcium alginate/poly (vinyl alcohol)/graphite hydrogel: thermal kinetics, combustion behavior and thermal insulation performance

2021

Liu, Jinru | Yu, Zhicai | He, Hualing | Wang, Yushu | Zhao, Yuhang

Design and development of fire-resistant composite materials with improved flame retardancy are critically needed for firefighters in fire protection fields. Herein, a novel fire-resistant composite hydrogel (FRCH) was fabricated based on calcium alginate (CA), poly (vinyl alcohol) (PVA) and expandable graphite (EG). The obtained FRCH material displayed prominent flame retardancy due to a large amount of heat was removed as contained water evaporation. Meanwhile, the EG in hydrogel occurred expansion to prevent heat transfer when exposed to fire. Results indicated that peak heat release rate and total release rate of FRCH decreased from 264.9 to 67.2 W/g and 15.4 to 12.1 KJ/g, respectively. The thermal kinetic behavior of FRCH was investigated by using Flynn-Wall-Ozawa (FWO) and Kissinger-Akahira-Sunose (KAS) models. TPP test further confirmed that introduction of EG in hydrogel prolonged the second-degree skin burn time for 2.73 s compared to without EG component. Besides, benefiting from the expansion behavior of EG when being burned, EG formed a conductive pathway and resulting in LED light up. This work provided an effective way to prepare flame retardant composite material with an early fire warning detection function, which may meet the requirements in firefighting fields.

Mostrar más [+]