Dissolution and recovery of cellulose from 1-butyl-3-methylimidazolium chloride in presence of water
2013
Iguchi, Masayuki | Aida, Taku Michael | Watanabe, Masaru | Smith, Richard L.
The dissolution and recovery of microcrystalline cellulose from 1-butyl-3-methylimidazolium chloride, [bmIm][Cl], were studied. At 90°C and 5h dissolution time, the regenerated cellulose could be recovered above 80wt% with a less than 10% decrease in the value of the viscosity-average degree of polymerization, DPᵥ, regardless of water content. Recovery ratio and DPᵥ of regenerated cellulose at 120°C decreased with time regardless of water content. The regenerated cellulose after dissolution at 120°C for 10h regardless of water content had cellulose II structure. Regenerated cellulose at short dissolution times or low temperature had high amorphous content. Both [bmIm][Cl] and [bmIm][Cl] with water act as a non-derivatizing solvent for microcrystalline cellulose at 90°C, and as a derivatizing solvent at 120°C. The main effect of added water on the dissolution of cellulose at high temperature was the promotion of cello-oligosaccharide and levoglucosan formation.
Mostrar más [+] Menos [-]Palabras clave de AGROVOC
Información bibliográfica
Este registro bibliográfico ha sido proporcionado por National Agricultural Library