Deformation twinning-induced dynamic recrystallization during laser powder bed fusion
2022
Sabzi, H.E. | Li, Xiao-Hui | Zhang, Chi | Fu, Hanwei | San-Martín, David | Rivera-Díaz del Castillo, P.E.J. | Royal Academy of Engineering | National Natural Science Foundation of China | Tsinghua University | Consejo Superior de Investigaciones Científicas [https://ror.org/02gfc7t72]
Nanotwin formation is observed during laser powder bed fusion (LPBF) of austenitic stainless steels fabricated with various process parameters. Transmission electron microscopy was employed to reveal the nature of such twins, which are formed due to the high strain rapid solidification inherent to LPBF. Dynamic recrystallization (DRX) was also activated during LPBF, and induced by the deformation nanotwins. A thermostatistical model is proposed to determine the critical conditions for twinning-induced DRX; the model is validated with the reported experimental results. This modelling approach offers a method to microstructurally engineer austenitic stainless steels for potential applications needing high strength and ductility.
Mostrar más [+] Menos [-]This work was supported by the Royal Academy of Engineering (RCSRF1718/5/32), and by EPSRC via DARE grant (EP/L025213/1). HF acknowledges the support by National Natural Science Foundation of China (51971011). CZ acknowledges the financial support by Tsinghua University research grant (20197050027). DSM is grateful to the Regional Government of Madrid (Spain) for the support via Mat4.0 project (S2018/NMT-4381).
Mostrar más [+] Menos [-]Información bibliográfica
Este registro bibliográfico ha sido proporcionado por Centro Nacional de Investigaciones Metalúrgicas